LNP VERTON PA66 RV00AESC compound
LNP™ VERTON™ PA66 RV00AESC compound
聚酰胺66
长玻璃纤维
SABIC Innovative Plastics (Europe-Africa-Middle)
 
产品说明
Also known as:LNP™ VERTON™ Compound RF-700-10 EM HS
Product reorder name:RV00AESC
 
LNP* VERTON* RV00AESC is a compound based on PA 66 resin containing Long Glass Fiber. Added features include; Easy Molding, Heat Stabilized.
 
增强填料:含长玻璃纤维
材料特点:易于成型,热稳定
塑料牌号:PA66 RV00AESC
定属记号:尼龙66
加工方法:注射成型
销售电话:185 5121 3137 谭经理
湘樟专卖:http://www.mba800.com/sujiao/pa66/verton/rv00aesc-compound.html
 
材料物性
MECHANICAL Value Unit Standard
Tensile Stress,break,5 mm/min 254 MPa ISO 527
Tensile Strain,break,5 mm/min 2 % ISO 527
Tensile Modulus,1 mm/min 17300 MPa ISO 527
Flexural Stress,break,2 mm/min 370 MPa ISO 178
Flexural Modulus,2 mm/min 15600 MPa ISO 178
IMPACT Value Unit Standard
Multiaxial Impact 152 cm-kgf ISO 6603
Izod Impact,unnotched 80*10*4 +23℃ 87 kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 38 kJ/m² ISO 180/1A
Izod Impact,notched 80*10*4 -40℃ 38 kJ/m² ISO 180/1A
THERMAL Value Unit Standard
CTE,23℃ to 60℃,flow 2.1E-05 1/℃ ISO 11359-2
CTE,23℃ to 60℃,xflow 5.5E-05 1/℃ ISO 11359-2
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm 257 ISO 75/Bf
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 253 ISO 75/Af
Relative Temp Index,Elec 105 UL 746B
Relative Temp Index,Mech w/impact 110 UL 746B
Relative Temp Index,Mech w/o impact 110 UL 746B
PHYSICAL Value Unit Standard
Mold Shrinkage,flow,24 hrs(5) 0.15 % ISO 294
Mold Shrinkage,xflow,24 hrs(5) 0.43 % ISO 294
Density 1.59 g/cm³ ISO 1183
Water Absorption,23℃/24hrs 0.9 % ISO 62-1
ELECTRICAL Value Unit Standard
Hot Wire Ignition{PLC) 0 PLC Code UL 746A
High Ampere Arc Ign,surface{PLC} 0 PLC Code UL 746A
FLAME CHARACTERISTICS Value Unit Standard
UL Recognized,94HB Flame Class Rating(3) 0.75 mm UL 94
Injection Molding Value Unit
Drying Temperature 80
Drying Time 4 hrs
Maximum Moisture Content 0.15-0.25 %
Melt Temperature 290-305
Front-Zone 3 Temperature 290-300
Middle-Zone 2 Temperature 290-300
Rear-Zone 1 Temperature 280-295
Mold Temperature 95-110
Back Pressure 0.2-0.3 MPa
Screw Speed 30-60 rpm
PA66 LNP™ VERTON™ COMPOUND
Crystalline polyamide 6,6 is one of the most widely used engineering plastics, combining easy processing with high impact strength, excellent thermal performance, and good economics. Provides good paintability and can be modified with tougheners and internal lubricants.