PA66 RV00AEXP compound 含长玻璃纤维

添加时间:2014-03-14  信息来源:http://www.mba800.com/  作者:苏州希普能塑料
LNP VERTON PA66 RV00AEXP compound
LNP™ VERTON™ PA66 RV00AEXP compound
聚酰胺66
长玻璃纤维
SABIC Innovative Plastics (Europe-Africa-Middle)
 
产品说明
Also known as:LNP™ VERTON™ Compound RF-700-10
Product reorder name:RV00AEXP
 
LNP* VERTON* RV00AEXP is a compound based on PA 66 resin containing Long Glass Fiber.
 
增强填料:含长玻璃纤维
塑料牌号:PA66 RV00AEXP
定属记号:尼龙66
加工方法:注射成型
销售电话:185 5121 3137 谭经理
湘樟专卖:http://www.mba800.com/sujiao/pa66/verton/rv00aexp-compound.html
 
材料物性
MECHANICAL Value Unit Standard
Tensile Stress,break,5 mm/min 268 MPa ISO 527
Tensile Strain,break,5 mm/min 2 % ISO 527
Tensile Modulus,1 mm/min 17600 MPa ISO 527
Flexural Stress,break,2 mm/min 405 MPa ISO 178
Flexural Modulus,2 mm/min 15500 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,unnotched 80*10*4 +23℃ 100 kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 35 kJ/m² ISO 180/1A
THERMAL Value Unit Standard
CTE,23℃ to 60℃,flow 2.4E-05 1/℃ ISO 11359-2
CTE,23℃ to 60℃,xflow 5.4E-05 1/℃ ISO 11359-2
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm 265 ISO 75/Bf
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 262 ISO 75/Af
Relative Temp Index,Elec 105 UL 746B
Relative Temp Index,Mech w/impact 110 UL 746B
Relative Temp Index,Mech w/o impact 110 UL 746B
PHYSICAL Value Unit Standard
Mold Shrinkage,flow,24 hrs(5) 0.24 % ISO 294
Mold Shrinkage,xflow,24 hrs(5) 0.79 % ISO 294
Density 1.57 g/cm³ ISO 1183
Water Absorption,23℃/24hrs 0.8 % ISO 62-1
ELECTRICAL Value Unit Standard
Hot Wire Ignition{PLC) 0 PLC Code UL 746A
High Ampere Arc Ign,surface{PLC} 0 PLC Code UL 746A
Comparative Tracking Index 0 V IEC 60112
FLAME CHARACTERISTICS Value Unit Standard
UL Recognized,94HB Flame Class Rating(3) 0.75 mm UL 94
Injection Molding Value Unit
Drying Temperature 80
Drying Time 4 hrs
Maximum Moisture Content 0.15-0.25 %
Melt Temperature 290-305
Front-Zone 3 Temperature 290-300
Middle-Zone 2 Temperature 290-300
Rear-Zone 1 Temperature 280-295
Mold Temperature 95-110
Back Pressure 0.2-0.3 MPa
Screw Speed 30-60 rpm
PA66 LNP™ VERTON™ COMPOUND
Crystalline polyamide 6,6 is one of the most widely used engineering plastics, combining easy processing with high impact strength, excellent thermal performance, and good economics. Provides good paintability and can be modified with tougheners and internal lubricants.