LNP VERTON PA66 RVL36SXS compound
LNP™ VERTON™ PA66 RVL36SXS compound
聚酰胺66
长玻璃纤维
SABIC Innovative Plastics (Europe-Africa-Middle)
 
产品说明
Also known as:LNP™ VERTON™ Compound RFL-8036
Product reorder name:RVL36SXS
 
LNP* VERTON* RVL36SXS is a compound based on PA 66 resin containing Long Glass Fiber, PTFE. Added features include; Internally Lubricated.
 
增强填料:含长玻璃纤维
含添加剂:聚四氟乙烯(PTFE)
材料特点:内部润滑
塑料牌号:PA66 RVL36SXS
定属记号:尼龙66
加工方法:注射成型
销售电话:185 5121 3137 谭经理
湘樟专卖:http://www.mba800.com/sujiao/pa66/verton/rvl36sxs-compound.html
 
材料物性
MECHANICAL Value Unit Standard
Tensile Stress,break,5 mm/min 185 MPa ISO 527
Tensile Strain,break,5 mm/min 2.3 % ISO 527
Tensile Modulus,1 mm/min 11200 MPa ISO 527
Flexural Stress,break,2 mm/min 275 MPa ISO 178
Flexural Modulus,2 mm/min 9300 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,unnotched 80*10*4 +23℃ 70 kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 33 kJ/m² ISO 180/1A
THERMAL Value Unit Standard
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm 265 ISO 75/Bf
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 261 ISO 75/Af
PHYSICAL Value Unit Standard
Density 1.53 g/cm³ ISO 1183
Injection Molding Value Unit
Drying Temperature 80
Drying Time 4 hrs
Maximum Moisture Content 0.15-0.25 %
Melt Temperature 290-305
Front-Zone 3 Temperature 290-300
Middle-Zone 2 Temperature 290-300
Rear-Zone 1 Temperature 280-295
Mold Temperature 95-110
Back Pressure 0.2-0.3 MPa
Screw Speed 30-60 rpm
PA66 LNP™ VERTON™ COMPOUND