PA66 RX02059 compound 含长玻纤和润滑油

添加时间:2014-03-14  信息来源:http://www.mba800.com/  作者:苏州希普能塑料
LNP VERTON PA66 RX02059 compound
LNP™ VERTON™ PA66 RX02059 compound
聚酰胺66
长玻璃纤维
SABIC Innovative Plastics (Europe-Africa-Middle)
 
LNP* VERTON* RX02059 is a compound based on PA 66 resin containing Long Glass Fiber, Proprietary Lubricant. Added features include; Internally Lubricated.
 
增强填料:含长玻璃纤维
含添加剂:专用润滑油
材料特点:内部润滑
塑料牌号:PA66 RX02059
定属记号:尼龙66
加工方法:注射成型
销售电话:185 5121 3137 谭经理
湘樟专卖:http://www.mba800.com/sujiao/pa66/verton/rx02059-compound.html
 
材料物性
MECHANICAL Value Unit Standard
Tensile Stress,yield,5 mm/min 217 MPa ISO 527
Tensile Strain,break,5 mm/min 2.4 % ISO 527
Flexural Stress,yield,2 mm/min 295 MPa ISO 178
Flexural Modulus,2 mm/min 13000 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,unnotched 80*10*4 +23℃ 70 kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 25 kJ/m² ISO 180/1A
THERMAL Value Unit Standard
CTE,23℃ to 60℃,flow 1.7E-05 1/℃ ISO 11359-2
CTE,23℃ to 60℃,xflow 6.5E-05 1/℃ ISO 11359-2
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm 261 ISO 75/Bf
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 258 ISO 75/Af
PHYSICAL Value Unit Standard
Mold Shrinkage,flow(5) 0.34 % SABIC Method
Mold Shrinkage,xflow(5) 1 % SABIC Method
Wear Factor Washer 15 10^-10 in^5-min/ft-lb-hr ASTM D 3702 Modified
Density 1.54 g/cm³ ISO 1183
Water Absorption,23℃/24hrs 0.8 % ISO 62-1
Injection Molding Value Unit
Drying Temperature 80
Drying Time 4 hrs
Maximum Moisture Content 0.15-0.25 %
Melt Temperature 290-305
Front-Zone 3 Temperature 290-300
Middle-Zone 2 Temperature 290-300
Rear-Zone 1 Temperature 280-295
Mold Temperature 95-110
Back Pressure 0.2-0.3 MPa
Screw Speed 30-60 rpm
PA66 LNP™ VERTON™ COMPOUND
Crystalline polyamide 6,6 is one of the most widely used engineering plastics, combining easy processing with high impact strength, excellent thermal performance, and good economics. Provides good paintability and can be modified with tougheners and internal lubricants.