PA66 RX06097 compound 含长玻纤,抗紫外线

添加时间:2014-03-14  信息来源:http://www.mba800.com/  作者:苏州希普能塑料
LNP VERTON PA66 RX06097 compound
LNP™ VERTON™ PA66 RX06097 compound
聚酰胺66
长玻璃纤维
SABIC Innovative Plastics (Europe-Africa-Middle)
 
产品说明
Also known as:LNP™ VERTON™ Compound RF70010 EM UV
Product reorder name:RX06097
 
LNP* VERTON* RX06097 is a compound based on PA 66 resin containing Long Glass Fiber. Added features include; Easy Molding, UV-Stabilized.
 
增强填料:含长玻璃纤维
材料特点:易于成型,抗紫外线稳定
塑料牌号:PA66 RX06097
定属记号:尼龙66
加工方法:注射成型
销售电话:185 5121 3137 谭经理
湘樟专卖:http://www.mba800.com/sujiao/pa66/verton/rx06097-compound.html
 
材料物性
MECHANICAL Value Unit Standard
Tensile Stress,break,5 mm/min 275 MPa ISO 527
Tensile Strain,break,5 mm/min 1.9 % ISO 527
Tensile Modulus,1 mm/min 17600 MPa ISO 527
Flexural Stress,break,2 mm/min 366 MPa ISO 178
Flexural Strain,break,2 mm/min 2.8 % ISO 178
Flexural Modulus,2 mm/min 15000 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,unnotched 80*10*4 +23℃ 90 kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 45 kJ/m² ISO 180/1A
THERMAL Value Unit Standard
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm 260 ISO 75/Bf
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 257 ISO 75/Af
PHYSICAL Value Unit Standard
Mold Shrinkage,flow,24 hrs(5) 0.32 % ISO 294
Mold Shrinkage,xflow,24 hrs(5) 0.76 % ISO 294
Density 1.59 g/cm³ ISO 1183
Water Absorption,23℃/24hrs 1 % ISO 62-1
Injection Molding Value Unit
Drying Temperature 80
Drying Time 4 hrs
Maximum Moisture Content 0.15-0.25 %
Melt Temperature 290-305
Front-Zone 3 Temperature 290-300
Middle-Zone 2 Temperature 290-300
Rear-Zone 1 Temperature 280-295
Mold Temperature 95-110
Back Pressure 0.2-0.3 MPa
Screw Speed 30-60 rpm
PA66 LNP™ VERTON™ COMPOUND
Crystalline polyamide 6,6 is one of the most widely used engineering plastics, combining easy processing with high impact strength, excellent thermal performance, and good economics. Provides good paintability and can be modified with tougheners and internal lubricants.