Plexiglas PMMA Satinice df33 7H

Plexiglas® PMMA Satinice df33 7H
聚甲基丙烯酸甲酯-丙烯酸
Evonik Industries AG
 
产品说明
PLEXIGLAS® Satinice df33 7H, based on PLEXIGLAS® 7H, is characterized by diffuse scattering of light.
 
Typical properties of impact modified PLEXIGLAS® molding compound are
﹒good flow
﹒high mechanical strength, surface hardness and mar resistance
﹒very good weather resistance.
 
Extruded parts from PLEXIGLAS® Satinice df33 7H are characterized by the following special properties:
﹒excellent light diffusion combined with excellent light transmission
﹒semi-gloss surfaces
﹒touch and fingerprint resistant.
 
Application:
Used for (Co-) extruding profiles and sheets for the construction, furniture and automotive industry.
 
Examples:
applications that call for light diffusion combined with optimum transmission and velvet matt surface appearance is desired.
 
含添加剂:冲击调节器
材料特点:High Hardness,改良抗撞击,高强度,中光泽度,表面光洁度佳,流动性佳,耐刮擦,耐气候影响,高清晰度
材料用途:家具,建筑应用领域,片材,汽车领域的应用,型材,照明漫射器
产品形式:颗粒料
产品外观:糙面磨光
加工方法:挤出
定属记号:丙烯酸 (PMMA)
塑料牌号:PMMA Satinice df33 7H
销售电话:185 5121 3137 谭经理
 
材料物性
物理性能 额定值 单位制 测试方法
密度 1.18 g/cm³ ISO 1183
溶化体积流率(MVR)(230℃/3.8 kg) 0.900 cm³/10min ISO 1133
机械性能 额定值 单位制 测试方法
拉伸模量 3300 MPa ISO 527-2/1
拉伸应力(断裂) 65.0 MPa ISO 527-2/5
拉伸应变(断裂) 4.0 % ISO 527-2/5
冲击性能 额定值 单位制 测试方法
简支梁缺口冲击强度(23℃) 17 kJ/m² ISO 179/1eU
热性能 额定值 单位制 测试方法
热变形温度      
0.45 MPa,未退火 101 ISO 75-2/B
1.8 MPa,未退火 99.0 ISO 75-2/A
维卡软化温度 102 ISO 306/B50
线形膨胀系数-流动(0 到 50℃) 0.000066 cm/cm/℃ ISO 11359-2
可燃性 额定值 单位制 测试方法
热灯丝点火温度 700 IEC 60695-2-13
光学性能 额定值 单位制 测试方法
光泽度2     ISO 2813
105° 16  
90° 9  
透射率3(3000 µm) 69.0 % ISO 13468-2
补充信息 额定值 单位制 测试方法
Half-Value Angle 34.0 ° DIN 5036
Scattering Power 0.470   DIN 5036
挤出 额定值 单位制
干燥温度 <90.0
干燥时间 2.0 到 3.0 hr
熔体温度 230 到 260
模具温度 230 到 260