Plexiglas PMMA Resist zk5HC

Plexiglas® PMMA Resist zk5HC
聚甲基丙烯酸甲酯-丙烯酸
Evonik Industries AG
 
产品说明
Product Profile:
PLEXIGLAS® Resist zk5HC is an amorphous, impact-modified thermoplastic molding compound (PMMA-I).
 
Typical properties of impact-modified
PLEXIGLAS® molding compounds are
﹒high weather resistance
﹒excellent transmission and clarity
﹒brilliant appearance
﹒the pleasant feel and sound of the moldings.
 
PLEXIGLAS® Resist zk5HC is characterized by the
﹒following special properties:
﹒high break resistance and impact strength
﹒best resistance to stress cracking of all impact-modified PLEXIGLAS® molding compounds.
 
Application:
Used for extruding and coextruding sheets and
profiles.
 
Examples:
extruded/coextruded sheets and profiles for automotive bodies and the sanitaryware sector (bathtubs and shower trays) or crystal-clear
luminaire covers for industrial plants that come into contact with aggressive media.
 
UL 黄卡2E65495-247820
含添加剂:冲击调节器
材料特点:高 ESCR(抗应力裂纹),高抗撞击,耐气候影响,高清晰度,外观良好
材料用途:保护性遮盖物,家用货品,片材,汽车防撞杆,汽车领域的应用,汽车外部零件,汽车外部装饰,型材
产品形式:颗粒料
加工方法:共挤出成型,挤出
定属记号:丙烯酸 (PMMA)
塑料牌号:PMMA Resist zk5HC
销售电话:185 5121 3137 谭经理
 
材料物性
物理性能 额定值 单位制 测试方法
密度 1.17 g/cm³ ISO 1183
溶化体积流率(MVR)(230℃/3.8 kg) 0.700 cm³/10min ISO 1133
吸水率     ISO 62
23℃,24 hr 1.9 %
平衡,23℃,50% RH 0.50 %
机械性能 额定值 单位制 测试方法
拉伸模量 2500 MPa ISO 527-2/1
拉伸应力(屈服) 63.0 MPa ISO 527-2/50
拉伸应变(屈服) 5.0 % ISO 527-2/50
断张率 28 % ISO 527-2
冲击性能 额定值 单位制 测试方法
简支梁缺口冲击强度(23℃) 55 kJ/m² ISO 179/1eU
热性能 额定值 单位制 测试方法
玻璃转化温度 108 ISO 11357-2
维卡软化温度 100 ISO 306/B50
线形膨胀系数-流动(0 到 50℃) 0.000090 cm/cm/℃ ISO 11359-2
可燃性 额定值   测试方法
UL 阻燃等级(1.60 mm) HB   UL 94
光学性能 额定值 单位制 测试方法
折射率 1.490   ISO 489
透射率3 92.0 % ISO 13468-2
补充信息 额定值   测试方法
Fire Rating B2   DIN 4102
注射 额定值 单位制
干燥温度 <90.0
干燥时间 2.0 到 3.0 hr
加工(熔体)温度 220 到 260
模具温度 50.0 到 70.0